Preparation and Properties of Calcium Hexaaluminate Porous Ceramics

作者：WANG Gang,ZHANG Qi,HAN Jianshen,YUAN Bo,LI Hongxia

摘要：In this paper,calcium hexaaluminate(CA6)porous ceramics were prepared by a foaming method combined with cement solidification molding.The effects of the foaming agent addition on the microstructure and the properties of the ceramics were studied.The results show that the microstructure and the porosity of the ceramics can be controlled by adjusting the addition of the foaming agent.As the addition of the foaming agent increased,the bulk density reduced from 1 g·cm^-3 to 0.35 g·cm^-3,the porosity increased from 70.4%to 89.6%,the compressive strength reduced from 18.46 MPa to 1.66 MPa,and the thermal conductivity at 1000°C decreased from 0.382 W·m^-1·K^-1 to 0.144 W·m^-1·K^-1.It is indicated that calcium hexaaluminate porous ceramics with low density,high strength and low thermal conductivity can be obtained by the foaming method.As the lining material of high temperature electric furnaces,the ceramic has excellent energy saving effect.

發文機構：State Key Laboratory of Advanced Refractories

關鍵詞：CALCIUMHEXAALUMINATEPOROUSCERAMICSFOAMINGMETHOD

分類號： TQ1[化學工程]