Phase Relationship at Subsolidus Temperature of MgO-MgAl2O4-ZrO2 Subsystem

作者：GAO Zhenxin

摘要：Three groups of cylinder specimens(φ10 mm×10 mm)with 20%,30%and 40%(by mass,the same hereinafter)of ZrO2,were prepared using analytically pure MgO,Al2O3 and ZrO2 powders as the starting materials.The specimens were fired at 1600℃for 5 h,1700℃for 0 h and 1800℃for 7 h,respectively.The microstructure of the MgO-MgAl2O4-ZrO2 subsystem was studied by FESEM.The results show that(1)in the temperature range of 1600-1700℃,solid phase reactions happen in the MgO-MgAl2O4-ZrO2 subsystem,leaving three phases:periclase,spinel and ZrO2(solid dissolving with Mg2+)co-existing;spinellization affects the densification;(2)the specimen with 40%ZrO2 fired at 1800℃has heterogeneous melting microstructure;some areas form typical ternary eutectic MgO-MgAl2O4-ZrO2 with composition of MgO 35.2%-37.2%,Al2O324.2%-26.6%,and ZrO237.2%-39.8%.

發文機構：Sinosteel Luoyang Institute of Refractories Research Co. Beijing Research and Development Center of Puyang Refractories Group Co.

關鍵詞：magnesia-magnesiumALUMINATEspinel-zirconiaSUBSYSTEMsubsolidusphaserelationshipmicrostructure

分類號： TG1[金屬學及工藝—金屬學]