Effect of tungsten oxide on ceria nanorods to support copper species as CO oxidation catalysts

作者：Yu'nan Li,Lin Gan,Rui Si

摘要：In this work,tungsten oxide with different concentrations(0,0.4 at%,2.0 at%and 3.2 at%)was introduced to the ceria nanorods via a deposition-precipitation(DP)approach,and copper species of ca.10 at%were sequentially anchored onto the modified ceria support by a similar DP route.The aim of the study was to investigate the effect of the amount of tungsten oxide(0,0.4 at%,2.0 at%,and 3.2 at%)modifier on the copper-ceria catalysts for CO oxidation reaction and shed light on the structure-activity relationship.By the aids of multiple characterization techniques including N2 adsorption,high-resolution transmission electron microscopy(HRTEM),powder X-ray diffraction(XRD),X-ray absorption fine structure(XAFS),and temperature-programmed reduction by hydrogen(H2-TPR)in combination with the catalytic performance for CO oxidation reaction,it is found that the copper-ceria samples maintain the crystal structure of the fluorite fcc CeO2 phase with the same nanorod-like morphology with the introduction of tungsten oxide,while the textural properties(the surface area,pore volume and pore size)of ceria support and copper-ceria catalysts are changed,and the oxidation states of copper and tungsten are kept the same as Cu2+and W6+before and after the reaction,but the introduction of tungsten oxide(WO3)significantly changes the metal-support interaction(transfer the CuOx clusters to Cu-[Ox]-Ce species),which delivers to impair the catalytic activity of copper-ceria catalysts for CO oxidation reaction.

發文機構：Hubei Collaborative Innovation Center for Advanced Organic Chemical Materials Zhangjiang Laboratory

關鍵詞：CoppercatalystCERIATungstenoxideCOoxidationStructure-activityrelationshipRareearths

分類號： X701[環境科學與工程—環境工程]O643.36[理學—物理化學]